扩链剂和相容剂 THYOSIL CXP5085 (低环氧当量重量)

THYOSIL CXP5085

澳洲幸运5平台 Chain extender扩链剂和相容剂

 

澳洲幸运5平台  

Description描述

 

THYOSIL CXP5085 is a multi-functional reactive polymer specially designed to restore molecular weight and intrinsic viscosity in degraded polymers.

THYOSIL CXP5085 澳洲幸运5平台allows to upgrade low quality recycle and can be used during processing to increase the melt strength of polyesters or polyamide.

THYOSIL CXP5085 also has high epoxy functionality, this allows for rapid reaction with condensation thermoplastics, resulting in higher molecular weight.

澳洲幸运5平台 THYOSIL CXP5085是一种多功能聚合物,专为在分解聚合物中恢复分子量和IV(特性粘度)而设计。

HYOSIL CXP 5085可以提升低质量的回收利用,可在加工过程中使用,以提高聚酯或聚酰胺的熔体强度。HYOSIL CXP 5085还具有高环氧官能度,这允许与缩合热塑性塑料快速反应,从而导致更高的分子量。

 

 

 

Advantages

 

ü       Higher regrind/recycle yield rate.更高的回收/回收再生率。

ü       Upgrade lower molecular weight polycondensate polymers.

澳洲幸运5平台 ü       升级较低分子量的缩聚物聚合物

ü       Compatibilization of polycondensate alloys.缩聚物合金的相容性

ü       Improved tensile strength.提高拉伸强度。

ü       Enhanced hydrolytic stability.增强水解稳定性。

 

 

Typical Properties典型值

澳洲幸运5平台 These properties are typical, do not constitute specifications

 

Appearance外观

Solid flake片状

Solids (%) 固含

>99

Tg (oC)玻璃化温度

54

Epoxy equivalent weight (g/mol)环氧值

285

澳洲幸运5平台  

 

Recommended dosage推荐用量

 

Plastic塑料

Application用于

Recommended Dosage推荐用量

(% w/w)

Polyesters (PET)聚酯

Fiber (staple and filament)

纤维(短纤维和长丝)

0.1 to 0.4

Injection/blow molding bottle

注塑/吹塑瓶

0.2 to 0.6

Sheet, tape and profile extrusion

片材,胶带和型材挤出

0.2 to 0.8

Film and bottle blow molding

薄膜和吹塑

0.2 to 0.8

Strapping打包带

0.2 to 0.8

Compatibilization PET/PA-nylon

聚酯与尼龙相容

0.5 to 1.0

Foam发泡

0.2 to 1.0

Polyesters (PETG, PBT, PLA, others)

Injection Molding注射成型

0.1 to 0.2

Fiber纤维

0.1 to 0.4

Profile extrusion型材挤出

0.1 to 0.6

Sheet and film片材和薄膜

0.3 to 1.0

Branching分枝

0.5 to 1.0

Foam发泡

0.2 to 1.0

Polyamides (nylon, PA 6, other)

聚酰胺(尼龙,PA 6,其他)

Injection Molding注射成型

0.1  to 0.2

Profile extrusion型材挤出

0.3 to 0.8

Sheet, film and tape

片材薄膜,胶带

0.4 to 1.0

Branching分枝

0.5 to 1.0

Compatibilization polyester/PA-nylon

增容聚酯/ PA尼龙

0.5 to 1.5

Polycarbonates (PC)

聚碳酸酯(PC

Injection molding注射成型

0.1 to 0.2

Hydrolytic stabilization水解稳定

0.3 to 0.8

Sheet and film片材和薄膜

0.4 to 1.2

Branching分枝

0.5 to 1.0

Other condensation thermoplastics (TPU, POM)

其他冷凝热塑性塑料(TPUPOM

Melt strength熔体强度

0.2 to 0.8

Stabilization稳定

0.2 to 1.0

 

Methods of Dosage剂量方法

 

 

Operation操作

Procedure步骤

1.       Dry blending

      干混

a)       Powder can be dry-blended with pre-dried and cold (<40°C) plastic pellets or with the aid of a low shear mixer such as a tumble mixer or conical mixer.

可以使用低剪切混合器(如滚筒式混合器或锥形混合器)将或母料与预干燥和冷(<40°C)塑料颗粒或薄片干混

b)      All solid forms of THYOSIL CXP5085 can be mixed with other materials in a high shear mixer below50°C.

可以在低于50的高剪切混合器中与其他材料混合

2.       Addition of THYOSIL CXP5085 on a single screw extruder, twin screw extruder or kneader

在单螺杆挤出机,双螺杆挤出机或knea上添加THYOSIL CXP 5085

a)       Dry-blend prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into mixing zone of the extruder  如(1)中制备的干混物可以体积计量,重量分析或直接进料到挤出机的混合区

b)      Gravimetric feed metering systems can be used to feed the product in a parallel stream with the plastic directly into the feeding zone of the extruder. Belt and disc feeders are particularly recommended.

Single Screw Feeders: Clearance of 3 to5 mmbetween the screw and the tube recommended.

Twin-Screw Feeders Non intermeshing spiral screw with 6mm clearance between the screw and the tube recommended. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below80°C.

重量进料计量系统可用于将平行流中的薄片或母粒澳洲幸运5下载形式直接进入挤出机的进料区。 特别推荐皮带和圆盘给料机

单螺杆给料机:推荐使用螺杆和管子间隙35 mm

双螺杆给料机推荐使用螺杆和管之间6mm间隙的非啮合螺旋螺杆。 通过保持管温度低于80消除在喉部或进料区聚集

c)       Volumetric Feeders: well calibrated feeders with variation of less than 0,5% are recommended. Clearance of 3 to5 mmbetween the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below80°C.

体积给料机:建议使用良好校准的变送量小于0.5%的进料器。 螺杆和管之间的间隙为35毫米也需要减少细粉。 通过保持管温度低于80消除在喉部或进料区聚集。

d)      Side feed systems and other types of forced dosing extruders may be employed with all solid product forms, except for fine powder, to feed the products downstream. Residence time recommendations are given below in reference to downstream feeds.除了细粉末之外,侧进料系统和其它类型的强制加料挤出机可以与所有固体澳洲幸运5下载形式一起使用,以在下游进料澳洲幸运5下载。 以下参考下游饲料给出停留时间建议

e)       Direct gravimetric/volumetric addition of the chain extender in any form to the plastic melt may be carried out through any suitable downstream venting or degassing port.

     任何形式的扩链剂直接重量/体积添加到塑料熔体可以通过任何合适的下游排气口或脱气口进行

3.       Addition during injection molding and combined injection-blow molding operations

    在注成型和组合注吹塑成型操作期间添加

a)       Dry-blends prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into the mixing zone of the injection molder.

      如(1)中制备的干混合物可以体积计量,重量分析或直接进料到注射成型机的混合区域

b)      Volumetric Feeders: Well calibrated feeders with variation of less than 0,5% are recommended, Clearance of 3 to5 mmbetween the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining temperatures below100°Cfor MB polymer carriers or80°Cfor wax carriers.

体积给料机:建议使用良好校准的变送量小于0.5%的进料器,螺杆和管之间的间隙为35 mm也需要减少细粉。 通过将MB聚合物载体的温度保持在低于100,对蜡载体保持温度低于80,可消除喉部或进料区的附聚

4.       Addition during polymerization and in other chemical reactors

在聚合过程中和其他化学反应中加入

a)       Additions of THYOSIL CXP5085 directly into polymerization reactors are feasible for some systems.某些系统可能将THYOSIL CXP5085直接加入到聚合反应釜中。

b)      Prior to any work including the use of THYOSIL CXP5085 in polymerization, we encourage you to discuss your system with our technical representatives.

 在使用THYOSIL CXP5085进行聚合工作之前,我们鼓励您与我们的技术代表讨论您的系统。

 

Processing conditions加工条件

 

 

Operation

Procedure

Pre-drying

预干燥

Pre-dry the base plastic at manufacturer’s recommended conditions.

推荐下预干燥基础塑料

In some instances small amounts of THYOSIL CXP5085 can be compensated for poor or incomplete drying, thus bringing robustness and saving to your operations. 在某些情况下,添加少量的THYOSIL CXP5085可以补偿不良或不完全的干燥,从而为您的操作带来方便和节省操作

Hygroscopicity: there is no evidence of bulk absorption of moisture over extended periods of time for THYOSIL CXP5085.

At normal conditions of temperature and relative humidity its surface reaches equilibrium saturation through adsorption at less than 0,25% of moisture.

At extreme conditions its surface reaches equilibrium saturation at less than 0,50% of moisture.

This means that THYOSIL CXP5085 can generally be processed without any drying, even after long exposure to drastic conditions bringing no more than 5ppm moisture per every 0,1% used.

吸湿性:THYOSIL CXP5085在长时间内没有大量吸收水分的迹象。在正常的温度和相对湿度条件下,其表面通过吸附小于0.25%的水分达到平衡饱和度。

在极端条件下其表面水分,在小于0.50%达到平衡饱和。这意味着即使经过长时间暴露于剧烈的条件下,THYOSIL CXP5085通常也可以进行加工处理,每0.1%使用不超过5ppm的水分。

Ins systems where moisture sensitivity is extreme, THYOSIL CXP5085 can be dried in a desiccant dryer ant30°Cfor 1 hour, prior to use.

在潮湿敏感度极高的系统中,THYOSIL CXP5085可以在干燥剂干燥器中于30 干燥1小时,然后再使用。

Extruder/injection molder temperature profile挤出机/注塑机温度曲线

Where feeding solid THYOSIL CXP5085 into the first zone of the extruder or infection molder, we recommend to operate this zone at20°Cto40 °Clower temperature than normal. This will prevent early melting and agglomeration of the additive.在将固体形式除母粒之外的固体THYOSIL CXP5085进入挤出机或感染模塑机的第一区域内,建议比常温低 ,在2040的温度下操作该区域。 这将防止添加剂的早期熔化和附聚。

All other zones should employ normal processing condition as recommended by the plastic’s manufacturer.

所有其他区域应采用塑料制造商推荐的正常加工条件。

Additive thermal stability

添加剂热稳定性

THYOSIL CXP5085 is thermally stable up to300°C. Above this temperature additive decomposition may occur.

THYOSIL CXP5085300°C以下是热稳定的。 高于此温度可能会发生分解

Residence time

停留时间

THYOSIL CXP5085 reacts quickly. Its reaction will be over 99% complete if at least 120sec residence time is provided at200°Cin a well-mixed system. Alternatively, 30 sec residence time at280°Cwill provide 99% completion.

THYOSIL CXP5085快速反应。 如果在200下在充分混合的系统中至少提供3分钟的停留时间,其反应将达到99%以上。 或者,在280下停留时间为45秒将完成99

These limits accommodate most extrusion and injection molding processed for the recommended thermoplastics and applications.

这些限制适用于为推荐的热塑性塑料和应用而加工的大多数挤出和注塑。

For use in polymerization reactors where residence time is over 5 minutes, see recommendations in section “Methods of Dosage”.

用于停留时间超过5分钟的聚合反应釜中,请参见“剂量方法”一节中的建议

 

·         THYOSIL CXP5085 澳洲幸运5平台should not be processed at temperatures higher than300°C

                                  不应在高于300°C的加工温度。

Extruder pressure effects挤出机压力效应

 

The use of THYOSIL CXP5085 inreactive extrusion or reactive injection molding operations increases significantly the molecular weight, this lead to an increase in melt viscosity, which in turn raises the pressure observed in the equipment.

The table below exemplifies the large increases in die pressure that are observed in PET as THYOSIL CXP5085 is added to a large extruder. Similar increases are expected in other plastics.

在反应性挤出或反应性注射成型工具中使用THYOSIL CXP5085显着增加了分子量,这导致熔体粘度的增加,从而提高了设备中观察到的压力。下表列举了将THYOSIL CXP5085加入到大型挤出机中时在PET中观察到的模具压力的大幅增加。 预计其他塑料类似增长。

 

 

Extrude variable

拉伸变量

PET Control

0,50%

THYOSIL CXP5085

1,00% THYOSIL CXP5085

1,50% THYOSIL CXP5085

Pressure die压模

1

1.45-1.65

1.90-2.30

2.20-2.60

Pressure screen

压力

1

1.45-1.65

1.90-2.30

2.20-2.60

Motor power draw

电机功率

1

1.08-1.10

1.13-1.18

1.17-1.21

 

The pressure increases both at the die and in front screen system may be 25% to 160% higher than typical operating pressure for higher usage levels.

Instantaneous pressure variations and spikes are due to large instantaneous changes in melt viscosity. At constant temperature, changes in melt viscosity are often due to variable feed rate and/or poor mixing.

在模具和前屏幕系统中的压力增加可以比用于较高使用水平的典型操作压力高25%至160%。瞬时压力变化和尖峰是由于熔体粘度的瞬间变化很大。 在恒定温度下,熔体粘度的变化通常是由于可变的进料速率和/或混合不良。

 

澳洲幸运5平台 The pressure and power draw changes with fluctuations in feed rate are calculated on the table below.压力和功率的变化随着进料速度的波动而计算如下表所示。

 

Extrude variable

拉伸变量

Steady feed within 5% of target value

稳定饲料在目标值的5%以内

Steady feed within 10% of target value

Steady feed within 20% of target value

Pressure die压模

± 2.0%

±4.3%

±9.0%

Pressure screen

压力

±2.5%

±4.5%

±9.2%

Pressure draw压差

±0.4%

±0.8%

±1.75%

 

 

Troubleshooting故障排除

 

Ø      In case of unexpected high pressure:如出现意想不到的高压:

 

1-       Decrease the feed rate of THYOSIL CXP5085.降低THYOSIL CXP5085的进料速度。

澳洲幸运5平台  

2-   Decrease the RPM. This decrease pressure on single screw extruders and flood-fed twin-screw extruders, and will decrease hating on starve-fed twin-screw extruders.  降低转速。 这对单螺杆挤出机和挤压双螺杆挤出机的压力降低,并且将减少对供给双螺杆挤出机的不适

澳洲幸运5平台 Slowly increase the temperature, starting from the die and then from the last to the zone.         

3-    缓慢升高温度,从模头开始,然后从最后到达区域。

 4-  With pressure under control, increase the THYOSIL CXP5085 feed slowly.

     在控制压力下,慢慢增加THYOSIL CXP 5085进料。

 5- For steady operation follow recommendations given in the section “extruder pressure effects”

澳洲幸运5平台     为了稳定运行,请参阅“挤出机压力效应”一节中给出的建议

 

Safe handling Information

Before using this product, read carefully the Material Safety Data Sheet (MSDS).

Note: The statements above are based on the current state of knowledge. They are intended to describe the product in relation to necessary safety precautions, and should not be used as a warranty of any specific property. Revision: March 2017.

© 版权所有·青岛澳洲幸运5官网有限公司   备案/许可证编号:鲁ICP备09036166号-2
地址:青岛市福州南路19号泛海名人广场4号楼603室      电话:86-0532-85788390      EMAIL:info@1msonline.com